Effect of nitriding conditions and operation temperatures on dry sliding wear properties of the aluminum extrusion die steel in the industry
Materials Today Communications, cilt.31, 2022 (SCI-Expanded, Scopus)
- Yayın Türü: Makale / Tam Makale
- Cilt numarası: 31
- Basım Tarihi: 2022
- Doi Numarası: 10.1016/j.mtcomm.2022.103628
- Dergi Adı: Materials Today Communications
- Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, Compendex, INSPEC
- Anahtar Kelimeler: Nitriding, Diffusion, Wear, Characterization, Mechanical properties
- Kırklareli Üniversitesi Adresli: Evet
Özet
Hot work tool steels are widely preferred in the hot extrusion of aluminum alloys. Nitriding of die steels in the aluminum extrusion industry is a well-accepted surface hardening method against surface wear and deformation. In this study, substrate material (DIN 1.2344 steel) is diffusion coated by salt bath nitriding method for 1 h, 2 h, and 3 h. The effect of different nitriding conditions on hardness, tensile and impact properties, wear behavior, and coefficient of friction is studied. Diffusion hardened surface is examined with different characterization techniques. The effect of nitriding time on diffusion layer thickness, tensile properties, impact energy, and wear resistance properties are investigated. It is shown that increasing nitriding time enables thicker diffusion layers that modify the adhesive's wear mechanism to abrasive. Increased nitride layer thickness resisted friction much more compared to less nitrided specimens. On the contrary of wear resistance, tensile properties are reduced due to the diffusion layer's notch effect.